Ultrafine NiFe2O4 powder fabricated from reverse microemulsion process

journal contribution
posted on 15.05.2003, 00:00 by Jiye Fang, Narayan Shama, Le Duc Tung, Eun Young Shin, Charles J. O’Connor, Kevin L. Stokes, Gabriel Caruntu, John B. Wiley, Leonard Spinu, Jinke Tang
NiFe2O4 ultrafine powder with high crystallinity has been prepared through a reverse microemulsion route. The composition in starting solution was optimized, and the resulting NiFe2O4 was formed at temperature of around 550–600 °C, which is much lower than that observed from the solid-state reaction. Magnetic investigation indicates that samples are soft magnetic materials with low coercivity and with the saturation magnetization close to the bulk value of Ni ferrite.